Blend Polyols for Wood Imitation

Rigid Polyurethane Blend Polyols for Wood Imitation

Rigid Polyurethane Blend Polyols for Wood Imitation

DFM-103

Products Introduction

"Wood Imitation" structure foam , is a new type of carving synthetic materials. It has high mechanical strength and hardness, simple molding process , high production efficiency and excellent appearance. 

Characteristics are as follows,

1. excellent repetition molding property.  It not only can mould certain shape size, but also mould  lifelike wood texture and other designs, good feel of touch 

2. appearance and feel close to wood , which could be planed, nailed, drilled, and carved patterns or designs . 

3. mould can only be produced using aluminum or steel, but can use silicon rubber, epoxy resin or other resin, which are low cost and easy machining. 

4. process is simple, fast, high efficiency of qualified. 

5. physical and mechanical properties is one of optimal synthesis wood produced by various polymer . Physical property can be controlled by adjusting the formula.

Physical Property

Appearance                Hydroxyl value                 mgKOH/g Viscosity          25°C        mPa.s Density           20 °C        g/ml Storage temperature            Storage stability                Month

Light yellow to brown yellow viscous liquid 250-400 600-1000 1.10±0.02 10-25 6

Recommended Ratio

	pbw
DFM-103 polyols Isocyanate	100 100-105

Reactivity Characteristics

Actual value varies as per processing conditions.

Rise time            s Gel time             s Tack free time        s Free density        kg/m3

50-70 140-160 200-220 90-250

Foam Performance

Moulding density   Curving  strength Compressive strength Tensile  strength Surface strength shrinking ratio

Kg/m3 MPa MPa MPa Shore D %

300-600 7-20 10-20 10-25 50-80 ≤0.3

Blend Polyols for Wood Imitation